Luachan cruas A.Material
| cruas Luach HRC |
cruas cuir luach air HRB |
cruas luach Vickers |
cruas luach Brinnell |
N / mm2 | Samhlaidhean DIN | ||
| -20 | 67 | 114 | 114 | 400 | C15 | ||
| -9 | 74 | 131 | 131 | 460 | C10 | ||
| 1 | 83 | 154 | 156 | 560 | C40 | stainless 303 | |
| 10 | 90 | 183 | 182 | 635 | |||
| 15 | 93 | 199 | 200 | 680 | C55 | 42CrMo4 | 32CrMo12 |
| 20 | 97 | 221 | 224 | 760 | 34CrNiMo6 14NiCr14 | ||
| 25 | 101 | 250 | 249 | 850 | 34CrNiMo6 ro-chùram | ||
| 30 | 105 | 278 | 276 | 955 | |||
| 35 | 109 | 320 | 323 | 1110 | |||
| 40 | 112 | 385 | 370 | 1270 | |||
| 45 | 115 | 460 | 427 | 1453 | C40 cruadhachadh |
||
| 50 | 118 | 535 | 497 | 1670 | 34CrNiMo6 cruadhachadh |
32 NiCrMo45 cruadhachadh |
42CrMo4 cruadhaichte |
| 55 | 639 | 545 | 1870 | C35 cruadhachadh | |||
| 57 | 694 | 576 | 1940 | ||||
| 60 | 746 | 601 | 2110 | 14NiCr14 cruadhachadh |
C10 cruadhachadh |
||
| 63 | 867 | 652 | 2220 | 32CrMo12 nitriteadh |
|||
| 65 | 940 | 682 | 2300 | ||||
| 67 | 1060 | 725 | 2400 | ||||
| 70 | 1170 | 760 | 2640 | ||||
B. Cruas Stuth (Làimhseachadh Teas)
Teòthachd |
dòigh |
ìre air fhaighinn |
|||
| Air a chuartachadh | |||||
| C40 | 830/860 ° C. | ann an amar ola airson 1h / 25 mm |
Cùm aig 650 ° C. + Cool airson uair a thìde ann an àmhainn no san adhar fosgailte |
||
| C55 | 810/840 ° C. | ann an amar ola airson 1h / 25 mm |
Cùm aig 650 ° C. + fionnar airson uair a thìde ann an àmhainn no san adhar fosgailte |
||
| 42CrMo4 | 860/890 ° C. | ann an amar ola airson 1h / 25 mm |
Cùm aig 690 ° C. + fionnar airson uair a thìde ann an àmhainn no san adhar fosgailte |
||
| 34CrNiMo6 | 820/850 ° C. | ann an amar ola airson 1h / 25 mm |
Cùm aig 650 ° C. + fionnar airson uair a thìde ann an àmhainn no san adhar fosgailte |
||
| Saimeant | |||||
| C10 <Ø100 | 900 gu 930 ° C airson 1h doimhneachd saimeant 0,2mm |
770/790 ° C. | 150 gu 200 ° C ann an amar ola 1h / 25 mm |
Cùm aig 650 ° C. + fionnar airson uair a thìde ann an àmhainn no san adhar fosgailte |
|
| C10> Ø100 | 900-930 ° C airson 1h doimhneachd saimeant 0,2mm |
900/930 ° C. | ann an amar ola 1h / 25 mm |
Cùm aig 650 ° C. + fionnar airson uair a thìde ann an àmhainn no san adhar fosgailte |
|
| 12NiCr14 | airson 1h doimhneachd saimeant 0,2mm |
820/840 ° C. | ann an amar ola 1h / 25 mm |
Cùm aig 650 ° C. + fionnar airson uair a thìde ann an àmhainn no san adhar fosgailte |
|
| * Na bi a ’stoc no a’ cleachdadh aig teòthachd eadar 250 agus 450 ° C. Tha na luachan uile tuairmseach |
|||||